Biofunctionalization of silicon surfaces by Hydrosilylation
Stable, densely packed organic monolayers covalently bonded directly to silicon surfaces currently receive significant interest in the field of biosensor applications, e.g. in biochemistry and biophysics, as they in principle allow the detection and utilization of charge transport across the silicon/organic interface. Preparation of such surfaces can be performed by hydrosilylation of H-terminated silicon with alkenes or alkynes. Beside crystalline silicon we try to use hydrogenated amorphous and microcrystalline silicon as a substrate material.
Hydrogenated amorphous silicon as an easily producible, large area electronic material is currently used for a variety of different applications, such as displays and solar cells. Organic surface modification of a-Si:H could therefore be an important issue for the fabrication of cheap biosensors in silicon technology.
Biofunctionalization of diamond surfaces
The diamond surface shows a unique property when it is hydrogen-terminated: surface conductivity, which makes it interesting for electronics, especially biosensors. Consisting of only carbon, diamond is a perfect biocompatible material.
Diamond surfaces are being functionalized for novel biosensor applications. Starting from the H-terminated surface a molecule (TFA-amine) with a protected amine group at the end is attached to the surface by a photochemical process. The success of this first step can be controlled by the use of XPS, trying to detect the fluorine (F1s) and nitrogen (N1s) peaks (see inset of fig.2). The next step is the deprotection of the amine group, making it reactive to the crosslinker which is attached in a further step. The deprotection can be monitored again by XPS controlling the nitrogen peak, while the fluorine peak disappeared. The final step is the attachment of an enzyme or a protein, or any other biomolecule (see fig. 2), for example the Green Fluorescent Protein (GFP). The coverage on a patterned surface can in this case be controlled optically with a fluorescence microscope (see fig.3).
Biofunctionalization of gallium nitride surfaces by silanisation
Self-assembled monolayers based on silanes can act as biocompatible and functional interlayers between oxidic solid surfaces and biomaterials. Monolayers of for example alkylsilane render the surface hydrophobic and allow the later deposition of polymer cushions for supported lipid membranes by Langmuir-Blodgett techniques. Aminosilane monolayers enable the imobilization of proteins by binding to the amino group via aldehyde agents.
Covalently coupled silane monolayers can be preparated by a self assemble process form organic solutions like toluene or chloroform if the surface is oxidic and provides hydroxyl groups. GaN surfaces fulfill this requirements after a thermal or chemical oxidation process and silane molecules from the ambient solution can form a covalnet siloxyl bond accompanied by the disposal of their head groups to the solution. Silanes with different active side groups, chains and chain length can be used for this surface functionalization.